Polysiloxane ZB95-11
Not sure which Zindn product is best for your project?
Our experts are here to guide you. Get a custom quote and expert advice today!
- Description
-
Polysiloxane ZB95-11
· A two-component, high-solid, super-weather-resistant topcoat made from acrylic modified polysiloxane resin and highly weather-resistant pigments.
· Industrial protective and decorative topcoat with excellent performance, suitable for steel structures or concrete surfaces in various harsh atmospheric environments, such as large steel structures, bridges, offshore platforms, tank outer walls, ship superstructures, petrochemical equipment, engineering machinery, and equipment, etc. It is especially suitable for surfaces with extremely high requirements for gloss and color retention.
Advantages of Polysiloxane Topcoat
· High decorative effect, strong UV resistance, and excellent weather resistance.
· The paint film is smooth, not easy to be stained with dirt, and has good self-cleaning performance;
· High solid content and low VOC;
· Excellent chemical resistance, good anti-penetration, and outstanding corrosion resistance;
· Meets the requirements of HG/T 4755 standard specifications.
Physical Constants
Type
Two components
Item no.
ZB95-11
Color
Customized
Gloss
Matt, Semi-gloss, High-gloss
Volume solids
75%
Solid by weight
≥85%
Density
1.38%
Recommended DFT
40μm-100μm
Theoretical coverage
0.147kg/㎡ (80μm DFT)
Touch-dry
2 hours (@25°C)
Application methods
Spray, Rolling, Brush
Application conditions
Temperature 5°C-38°C, humidity <80%
Shelf life
12 months from manufacture date (unopened)
Pot life
4 hours (@25°C)
Pack
24(20+4) kgs/Kit
Mixing ratio
5:1 (base: hardener)
Storage
In a cool and ventilated place
MOQ
500kgs
Country of Origin
Jiangsu province, China
Polysiloxane Topcoat Protective System
2 Coats System
· Epoxy primer (60μm-300μm) + Polysiloxane (40μm-100μm)
· Epoxy graphene zinc (60μm-160μm) + Polysiloxane (40μm-100μm)
3 Coats System
· Epoxy primer (60μm-300μm) + MIO coat (100μm -180μm) + Polysiloxane (40μm-100μm)
· Epoxy zinc primer (60μm-80μm) + MIO coat (100μm -180μm) + Polysiloxane (40μm-100μm)
· Epoxy graphene zinc (60μm-160μm) + MIO coat (100μm -180μm) + Polysiloxane (40μm-100μm)
· ZINDN96-1 (60μm-80μm) + ZINDN sealer (60μm -120μm) + Polysiloxane (40μm-100μm)
Applications
Application Notes
1. The specified thinner must be used and applied on the compatible primer or intermediate paint, otherwise, it will affect the product quality.
2. During the paint preparation process, it is strictly forbidden to contact with water, acid, alkali, alcohol, etc.
Component B is very easy to react with water and other substances. The packaging barrel of the remaining component B after preparation must be tightly covered.
3. During the application and drying, and curing period, the relative humidity shall not be greater than 85%.
4. During the application process, or shortly after the application, the surface is subjected to water vapor condensation and sudden cooling, which will cause the surface to lose gloss, turn white, and deteriorate in quality.
5. When applications are made by either roller or brush, multiple coats may be required to obtain a complete covering effect, especially for some lead-free bright colours such as yellow, orange, etc.
Related Products
Message
Note: Please leave your contact information and our professionals will contact you as soon as possible!
Contact Us
Headquarters Tel:
Business Hotline:
E-mail:
WhatsApp/Wechat:
Quick Navigation
Online Message
If you have any product related questions, please feel free to contact us!
Copyright © 2025 Wuxi Huadong Zindn Science and Technology Co., Ltd.